DEEMEX Series
DMX 100
C. (%) : 3.2 – 4.7
Cr. (%) : 22 – 27
Other : Mn, Fe
Hardness Rockwell : 50 – 56
Plate Thickness
Plate : >=3mm
Coating : >=3mm
DMX 105
C. (%) : 4.5 – 5.5
Cr. (%) : 27 – 32
Other : Mn, B, Fe
Hardness Rockwell : 56 – 60
Plate Thickness
Plate : >=3mm
Coating : >=3mm
DMX 110
C. (%) : 4.5 – 5.9
Cr. (%) : 32 – 37
Other : Mn, B, Mo, Fe
Hardness Rockwell : 60 – 64
Plate Thickness
Plate : >=3mm
Coating : >=3mm
DMX 413
C. (%) : 3.3 – 4.7
Cr. (%) : 22 – 32
Nb. (%) : 2.7 – 3.3
Other : Mn, Mo, Fe
Hardness Rockwell : 58 – 62
Plate Thickness
Plate : >=3mm
Coating : >=3mm
DMX 415
C. (%) : 3.5 – 4.9
Cr. (%) : 22 – 32
Nb. (%) : 4.7 – 5.3
Other : Mn, Mo, Fe
Hardness Rockwell : 60 – 64
Plate Thickness
Plate : >=3mm
Coating : >=3mm
DMX 510
C. (%) : 4.2 – 5.9
Cr. (%) : 18 – 28
Nb. (%) : 6.7 – 7.3
Other : Mn, B, Mo, Fe
Hardness Rockwell : 62 – 67
Plate Thickness
Plate : >=5mm
Coating : >=3mm
Standard DEEMEX Plates
| STANDARD BASE SHEET DIMENSIONS |
STANDARD CLAD DIMENSIONS | STANDARD BASE MATERIAL | OPTIONAL BASE MATERIALS |
|---|---|---|---|
| 1000 x 2000mm 1250 x 2500mm 1500 x 3000mm |
950 x 1950mm (±30mm) 1200 x 2450mm (±30mm) 1450 x 2950mm (±30mm) |
S235JR |
Wear Resistant Steels Stainless Steels P265GH P275GH |
Production Process
Our engineers have 40 years of experience in constructions. So they have the best solutions in wear problems. DEEMEX Plates are reducing maintenance and operating costs, providing longer service life. In our production line, which is suited in Greece (EU), we assure quality by analyzing the microstructure and chemical composition in every batch.
All the production is fully automated and all raw materials are checked for purity and test certificates. The finished product is checked for composition, carbide content, tolerances, crack dimension and straightness from our fully equipped testing lab.
We deliver DEEMEX Plates with all certificates DIN 50049-2.2 for coating and EN 1024:2004-3.1 for base plates, according to EN ISO 9001:2008.
The newest production line of DEEMEX Plates employs PLC controlled systems ensuring uniform coating bed width and various welding shape imprints.
DEEMEX Plates outlast in high abrasion applications quench and tempered steels by up to 9 times and up to 42 times mild steel, according to ASTM G65-00 standard testing
Typical Applications
After many years of economic losses due to abrasion, highly industrialized countries embrace Hard Facing Technology. This is because Hard Facing technology reduces maintenance costs, minimizes the number of repairs, reduces downtime and generally makes the life of engineers easier.
DEEMEX technology also reduces investment costs because carbon steel (S235JR) is used as base material even under highly abrasive conditions. The industries that mainly profited from this technological achievement are:
- Cement Industries
- Coal-fired Electric Power Stations
- Iron and Steel Industries
- Brickworks
- Quarries, Sand and Gravel Works
- Mining and Opencast Mining Industries
- Waste Incineration Industries
- Recycling Industries
| DEEMEX SERIES | ||
|---|---|---|
| WEAR PLATES | HARDNESS ROCKWELL |
RECOMMENDED APPLICATIONS |
| DMX 100 | 50-56 | Crusher parts, bucket lips, conveyor screws |
| DMX 105 | 56-60 | Chutes, Feeders and Scrolls, Mixer blades and components, Rotor blades for fans in cement industries, Wearing parts for Dedusting systems, Pipes, Scrapers, Mills |
| DMX 110 | 60-64 | Dredge Pump parts, Hoppers, Crusher Rolls, Screw Conveyors,,Blast furnace, Sinter plant, Cement kilns,Exhaust fan blades, Pearlite crushers, Mixing tools, Bunker cladding, Excavator shovels, Shovel bucket teeth |
| DMX 413 | 58-62 | Screens, Sinter Crushers, Mixer Components, Coke Pushers, Hot Dust Ducts |
| DMX 415 | 60-64 | Screens, Sinter Crushers, Sinter Bars, Mixer Components, Hot Dust Ducts |
| DMX 510 | 62-67 | Impellers, Pan mixers, Chutes, Tubes, Screw Conveyors, Fans |
| The Wear Plate Series (DMX100, 105, 110) comes with Standard Base Material | ||